標(biāo)準(zhǔn)編號:	GB/T 11253-2019
中文名稱:	碳素結(jié)構(gòu)鋼冷軋鋼板及鋼帶
英文名稱:	Cold-rolled sheet and strip of carbon structural steels
行業(yè)分類:	GB    國家標(biāo)準(zhǔn)
ICS分類:	77.140.50 77.140.50    扁平鋼和半成品 77.140.50
發(fā)布機(jī)構(gòu):	國家市場監(jiān)督管理總局 國家標(biāo)準(zhǔn)化管理委員會
發(fā)布日期:	2019-10-18
實(shí)施日期:	2020-9-1
標(biāo)準(zhǔn)狀態(tài):	valid
替代舊標(biāo)準(zhǔn):	GB/T 11253-2007 碳素結(jié)構(gòu)鋼冷軋薄鋼板及鋼帶 GB 716-1991 碳素結(jié)構(gòu)鋼冷軋鋼帶
翻譯語言:	英文
文件格式:	PDF
中文字符數(shù):	11000 字
翻譯價(jià)格(元):	290.0
交付時(shí)間:	付款后 1 個(gè)工作日

Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative. This standard is developed in accordance with the rules given in GB/T 1.1-2009. This standard replaces and combines GB/T 11253-2007 Cold-rolled sheets and strips of carbon structural steels and GB/T 716-1991 Cold-rolled carbon structural steel strips, with respect to which, the following main technical changes have been made: ——the thickness range of steel sheets and strips and the width range of cold-rolled narrow steel sheets and strips are modified (see Clause 1; Clause 1 of GB/T 11253-2007); ——the classification and code of surface structure are modified (see 3.2; 3.2 of GB/T 11253-2007); ——the order contents are modified by adding surface structure types and oiling requirements (see Clause 4; Clause 4 of GB/T 11253-2007); ——the dimension, shape, weight and tolerance of cold-rolled narrow steel sheets and strips and are modified (see Table 1; Table 1 of GB/T 716-1991); ——Grade Q325 and corresponding chemical composition, mechanical properties and processing properties are added (see Tables 2, 3 and 4); ——technical requirements for cold-rolled narrow steel sheets and strips are modified (see Table 3; Table 3 of GB/T 716-1991); ——the requirements for surface structure are added (see Table 6); ——the rounding-off requirements for numerical values are added (see 8.4); ——the requirements for types of quality certificates of steel sheets and strips are deleted (see Clause 9 of GB/T 11253-2007). This standard was proposed by China Iron and Steel Industry Association. This standard is under jurisdiction of the National Technical Committee on Iron and Steel of Standardization Administration of China (SAC/TC 183). The previous editions of this standard are as follows: ——GB/T 11253-1989 and GB/T 11253-2007; ——GB/T 716-1983 and GB/T 716-1991. Cold-rolled sheet and strip of carbon structural steels 1 Scope This standard specifies the order contents, dimension, shape and weight, technical requirements, test methods, inspection rules, as well as packaging, marking and quality certificate of cold-rolled steel sheets and strips of carbon structural steels. This standard is applicable to cold-rolled thin sheets and strips of carbon structural steels with a thickness of not greater than 4mm, including cold-rolled wide strips, sheared sheets and slit wide strips with a width of not less than 600mm (hereinafter referred to as wide steel sheets and strips) as well as cold-rolled narrow strips and sheared sheets with a width of 250~<600mm (hereinafter referred to as narrow steel sheets and strips). It may serve as a reference for the single cold-rolled steel sheet with a width of not less than 600mm. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. GB/T 222 Permissible tolerances for chemical composition of steel products GB/T 223.3 Methods for chemical analysis of iron, steel and alloy - The diantipyryl methane phosphomolybdate gravimetric method for the determination of phosphorus content GB/T 223.9 Iron, steel and alloy - Determination of aluminium content - Chrome azurol S photometric method GB/T 223.11 Iron, steel and alloy - Determination of chromium content - Visual titration or potentiometric titration method GB/T 223.18 Methods for chemical analysis of iron, steel and alloy - The sodium thiosulfate separation iodimetric method for the determination of copper content GB/T 223.19 Methods for chemical analysis of iron, steel and alloy - The neocuproine-chloroform extraction photometric method for the determination of copper content GB/T 223.23 Iron, steel and alloy - Determination of nickel content - The dimethylglyoxime spectrophotometric method GB/T 223.37 Methods for chemical analysis of iron, steel and alloy - The indophenol blue photometric method for the determination of nitrogen content after distillation separation GB/T 223.58 Methods for chemical analysis of iron, steel and alloy - The sodium arsenite-sodium nitrite titrimetric method for the determination of manganese content GB/T 223.59 Iron, steel and alloy - Determination of phosphorus content - Bismuth phosphomolybdate blue spectrophotometric method and antimony phosphomolybdate blue spectrophotometric method GB/T 223.60 Methods for chemical analysis of iron, steel and alloy - The perchloric acid dehydration gravimetric method for the determination of silicon content GB/T 223.63 Methods for chemical analysis of iron, steel and alloy - The sodium (potassium) periodate photometric method for the determination of manganese content GB/T 223.64 Iron, steel and alloy - Determination of manganese content - Flame atomic absorption spectrometric method GB/T 223.68 Methods for chemical analysis of iron, steel and alloy - The potassium iodate titration method after combustion in the pipe furnace for the determination of sulfur content GB/T 223.71 Methods for chemical analysis of iron, steel and alloy - The gravimetric method after combustion in the pipe furnace for the determination of carbon content GB/T 223.72 Iron, steel and alloy - Determination of sulfur content - Gravimetric method GB/T 228.1-2010 Metallic materials - Tensile testing - Part 1: Method of test at room temperature GB/T 232 Metallic materials - Bend test GB/T 247 General rule of package, mark and certification for steel plates (sheets) and strips GB/T 708 Dimension, shape, weight and tolerance for cold-rolled steel strip and sheet GB/T 2523 Measuring method of surface roughness and peak count for cold-rolled metal sheet (strip) GB/T 2975 Steel and steel products - Location and preparation of samples and test pieces for mechanical testing GB/T 4336 Carbon and low-alloy steel - Determination of multi-element contents - Spark discharge atomic emission spectrometric method (routine method) GB/T 8170 Rules of rounding off for numerical values & expression and judgment of limiting values GB/T 15391 Dimension, shape and tolerances for cold-rolled steel strips with a width less than 600mm GB/T 17505 Steel and steel products - General technical delivery requirements GB/T 20066 Steel and iron - Sampling and preparation of samples for the determination of chemical composition GB/T 20123 Steel and iron - Determination of total carbon and sulfur content - Infrared absorption method after combustion in an induction furnace (routine method) GB/T 20125 Low-alloy steel - Determination of multi-element contents - Inductively coupled plasma atomic emission spectrometric method 3 Classification and code 3.1 According to the surface quality, steel sheets and strips are classified into: ——relatively high grade surface FB; ——high grade surface FC. 3.2 According to the surface structure, steel sheets and strips are classified into: ——ultra-smooth surface b; ——shiny surface B; ——pitted surface D. Note: ultra-smooth surface is only applicable to narrow strip and its sheared sheets. 4 Order contents 4.1 Contracts or orders made based on this standard shall cover the following contents: a) product name (wide or narrow sheet or strip); b) No. of this standard; c) grade; d) dimension and precision; e) surface quality grade; f) surface structure; g) oiling; h) edge condition (trimmed EC or untrimmed EM); i) packaging method; j) weight; k) use; l) special requirements. 4.2 If information, e.g., dimension and unevenness precision, surface quality grade, surface structure type, edge condition and packaging method, is not specified in the order contract, the oiled and trimmed sheet or strip with common dimension and unevenness precision, relatively high grade surface quality and pitted surface structure under this standard shall be supplied, and packaged according to the method provided by the supplier. 5 Dimension, shape and weight 5.1 The dimension, shape, weight and tolerance of wide steel sheets and strips shall meet those specified in GB/T 708. 5.2 The dimension, shape, weight and tolerance of narrow steel sheets and strips shall meet those specified in GB/T 15391, wherein, the width tolerance shall meet those specified in Table 1.

Foreword i 1 Scope 2 Normative references 3 Classification and code 4 Order contents 5 Dimension, shape and weight 6 Technical requirements 7 Test methods 8 Inspection rules 9 Packaging, marking and quality certificate

ICS 77.140.50 H 46 中華人民共和國國家標(biāo)準(zhǔn) GB/T 11253—2019 代替GB/T 11253—2007，GB/T 716—1991 碳素結(jié)構(gòu)鋼冷軋鋼板及鋼帶 Cold-rolled sheet and strip of carbon structural steels 2019-10-18發(fā)布 2020-09-01實(shí)施 國家市場監(jiān)督管理總局 中國國家標(biāo)準(zhǔn)化管理委員會 發(fā)布 前言 本標(biāo)準(zhǔn)按照GB/T 1.1—2009給出的規(guī)則起草。 本標(biāo)準(zhǔn)代替GB/T 11253—2007《碳素結(jié)構(gòu)鋼冷軋薄鋼板及鋼帶》和GB/T 716—1991《碳素結(jié)構(gòu)鋼冷軋鋼帶》。本標(biāo)準(zhǔn)對GB/T 11253—2007《碳素結(jié)構(gòu)鋼冷軋薄鋼板及鋼帶》和GB/T 716—1991《碳素結(jié)構(gòu)鋼冷軋鋼帶》進(jìn)行了合并。與GB/T 11253—2007和GB/T 716—1991相比，主要技術(shù)變化如下： ——修改了鋼板及鋼帶的厚度范圍和冷軋窄鋼板及鋼帶的寬度范圍(見第1章，GB/T 11253—2007的第1章)； ——修改了表面結(jié)構(gòu)分類及代號(見3.2，GB/T 11253—2007的3.2)； ——修改了訂貨內(nèi)容，增加表面結(jié)構(gòu)類型和涂油規(guī)定(見第4章，GB/T 11253—2007的第4章)； ——修改冷軋窄鋼板及鋼帶的尺寸、外形、重量及允許偏差(見表1，GB/T 716—1991的表1)； ——增加了Q325牌號及相應(yīng)的化學(xué)成分、力學(xué)性能和工藝性能(見表2、表3、表4)； ——修改了冷軋窄鋼板及鋼帶的技術(shù)要求(見表3，GB/T 716—1991的表3)； ——增加了表面結(jié)構(gòu)要求(見表6)； ——增加了數(shù)值修約要求(見8.4)； ——?jiǎng)h除了鋼板及鋼帶的質(zhì)量證明書類型規(guī)定(見GB/T 11253—2007的第9章)。 本標(biāo)準(zhǔn)由中國鋼鐵工業(yè)協(xié)會提出。 本標(biāo)準(zhǔn)由全國鋼標(biāo)準(zhǔn)化技術(shù)委員會(SAC/TC 183)歸口。 本標(biāo)準(zhǔn)所代替標(biāo)準(zhǔn)的歷次版本發(fā)布情況為： ——GB/T 11253—1989、GB/T 11253—2007； ——GB/T 716—1983、GB/T 716—1991。 碳素結(jié)構(gòu)鋼冷軋鋼板及鋼帶 1 范圍 本標(biāo)準(zhǔn)規(guī)定了碳素結(jié)構(gòu)鋼冷軋鋼板及鋼帶的訂貨內(nèi)容、尺寸、外形、重量、技術(shù)要求、試驗(yàn)方法、檢驗(yàn)規(guī)則、包裝、標(biāo)志及質(zhì)量證明書。 本標(biāo)準(zhǔn)適用于厚度不大于4 mm的碳素結(jié)構(gòu)鋼冷軋薄鋼板及鋼帶，包括寬度不小于600 mm的冷軋寬鋼帶及剪切鋼板、縱切鋼帶(簡稱寬鋼板及鋼帶)及寬度范圍為250 mm～<600 mm的冷軋窄鋼帶及剪切鋼板(簡稱窄鋼板及鋼帶)。寬度不小于600 mm的單張冷軋鋼板亦可參照執(zhí)行。 2規(guī)范性引用文件 下列文件對于本文件的應(yīng)用是必不可少的。凡是注日期的引用文件，僅注日期的版本適用于本文件。凡是不注日期的引用文件，其最新版本(包括所有的修改單)適用于本文件。 GB/T 222鋼的成品化學(xué)成分允許偏差 GB/T 223.3 鋼鐵及合金化學(xué)分析方法 二安替比林甲烷磷鉬酸重量法測定磷量 GB/T 223.9 鋼鐵及合金 鋁含量的測定 鉻天青S分光光度法 GB/T 233.11 鋼鐵及合金 鉻含量的測定 可視滴定或電位滴定法 GB/T 223.18鋼鐵及合金化學(xué)分析方法 硫代硫酸鈉分離-碘量法測定銅量 GB/T 223.19 鋼鐵及合金化學(xué)分析方法 新亞銅靈三氯甲烷萃取光度法測定銅量 GB/T 223.23鋼鐵及合金 鎳含量的測定 丁二酮肟分光光度法 GB/T 223.37鋼鐵及合金化學(xué)分析方法 蒸餾分離靛酚藍(lán)光度法測定氮量 GB/T 223.58鋼鐵及合金化學(xué)分析方法 亞砷酸鈉-亞硝酸鈉滴定法測定錳量 GB/T 223.59 鋼鐵及合金 磷含量的測定 鉍磷鉬藍(lán)分光光度法和銻磷鉬藍(lán)分光光度法 GB/T 223.60鋼鐵及合金化學(xué)分析方法 高氯酸脫水重量法測定硅含量 GB/T 223.63鋼鐵及合金化學(xué)分析方法 高碘酸鈉(鉀)光度法測定錳量 GB/T 223.64鋼鐵及合金 錳含量的測定 火焰原子吸收光譜法 GB/T 223.68 鋼鐵及合金化學(xué)分析方法 管式爐內(nèi)燃燒后碘酸鉀滴定法測定硫含量 GB/T 223.71 鋼鐵及合金化學(xué)分析方法 管式爐內(nèi)燃燒后重量法測定碳含量 GB/T 223.72鋼鐵及合金 硫含量的測定 重量法 GB/T 228.1—2010 金屬材料 拉伸試驗(yàn) 第1部分：室溫試驗(yàn)方法 GB/T 232 金屬材料 彎曲試驗(yàn)方法 GB/T 247鋼板和鋼帶包裝、標(biāo)志及質(zhì)量證明書的一般規(guī)定 GB/T 708冷軋鋼板和鋼帶的尺寸、外形、重量及允許偏差 GB/T 2523冷軋金屬薄板(帶)表面粗糙度和峰值數(shù)的測量方法 GB/T 2975鋼及鋼產(chǎn)品 力學(xué)性能試驗(yàn)取樣位置及試樣制備 GB/T 4336碳素鋼和中低合金鋼 多元素含量的測定 火花放電原子發(fā)射光譜法(常規(guī)法) GB/T 8170數(shù)值修約規(guī)則與極限數(shù)值的表示和判定 GB/T 15391寬度小于600 mm冷軋鋼帶的尺寸、外形及允許偏差 GB/T 17505鋼及鋼產(chǎn)品 交貨一般技術(shù)要求 GB/T 20066鋼和鐵 化學(xué)成分測定用試樣的取樣和制樣方法 GB/T 20123鋼鐵 總碳硫含量的測定 高頻感應(yīng)爐燃燒后紅外吸收法(常規(guī)方法) GB/T 20125 低合金鋼 多元素含量的測定 電感耦合等離子體原子發(fā)射光譜法 3分類及代號 3.1 鋼板及鋼帶按表面質(zhì)量分為： ——較高級表面FB； ——高級表面FC。 3.2鋼板及鋼帶按表面結(jié)構(gòu)分為： ——超平滑b； ——光亮表面B； ——麻面D。 注：超平滑僅適用于窄鋼帶及其剪切鋼板。 4訂貨內(nèi)容 4.1 按本標(biāo)準(zhǔn)訂貨的合同或訂單應(yīng)包括下列內(nèi)容： a)產(chǎn)品名稱(寬鋼板、寬鋼帶、窄鋼板或窄鋼帶)； b)標(biāo)準(zhǔn)編號； c)牌號； d)尺寸規(guī)格及精度； e)表面質(zhì)量級別； f)表面結(jié)構(gòu)； g)涂油； h)邊緣狀態(tài)(切邊EC、不切邊EM)； i)包裝方式； j)重量； k)用途； l)特殊要求。 4.2如訂貨合同中未注明尺寸及不平度精度、表面質(zhì)量級別、表面結(jié)構(gòu)種類、邊緣狀態(tài)和包裝方式等信息，則本標(biāo)準(zhǔn)產(chǎn)品按普通級尺寸及不平度精度、較高級表面質(zhì)量、表面結(jié)構(gòu)為麻面的涂油切邊鋼板或鋼帶供貨，并按供方提供的包裝方式包裝。 5尺寸、外形、重量 5.1 寬鋼板及鋼帶的尺寸、外形、重量及允許偏差應(yīng)符合GB/T 708的規(guī)定。 5.2窄鋼板及鋼帶的尺寸、外形、重量及允許偏差應(yīng)符合GB/T 15391的規(guī)定，其中寬度允許偏差應(yīng)符合表1的規(guī)定。 表1 窄鋼板及鋼帶的寬度允許偏差 單位為毫米 鋼帶寬度 允許偏差a 不切邊 切邊 250～350 +3.0 -2.0 +1.0 0 >350～450 ±4.0 >450～<600 ±5.0 a根據(jù)需方要求，經(jīng)供需雙方協(xié)商，鋼帶寬度偏差可在公差范圍內(nèi)進(jìn)行適當(dāng)調(diào)整。 6 技術(shù)要求 6.1牌號和化學(xué)成分 6.1.1 鋼的牌號和化學(xué)成分(熔煉分析)應(yīng)符合表2規(guī)定。 表2鋼的牌號及化學(xué)分析 牌號 化學(xué)成分(質(zhì)量分?jǐn)?shù))/％，不大于 C Si Mn Pa S Ni Cr Cu N Q195 0.12 0.30 0.50 0.035 0.035 0.30 0.30 0.30 0.012 Q215 0.15 0.35 1.20 0.035 0.035 Q235 0.22 0.35 1.40 0.035 0.035 Q275 0.24 0.35 1.50 0.035 0.035 Q325 0.20 0.55 1.60 0.035 0.025 a經(jīng)需方同意，P為固溶強(qiáng)化元素添加時(shí)，上限應(yīng)不大于0.12％。 6.1.2 當(dāng)采用鋁脫氧時(shí)，鋼中酸溶鋁(Als)含量應(yīng)不小于0.015％，或總鋁(Alt)含量應(yīng)不小于0.020％。 6.1.3鋼中殘余元素鉻、鎳、銅含量如供方能保證，可不進(jìn)行分析。 6.1.4鋼中氮元素含量如供方保證，可不進(jìn)行分析。如果鋼中酸溶鋁(Als)含量不小于0.015％或總鋁(Alt)含量不小于0.020％，或添加了其他具有固氮作用的合金元素，氮元素含量不作限制，固氮元素應(yīng)在質(zhì)量證明書中注明。 6.1.5在保證鋼材力學(xué)性能符合本標(biāo)準(zhǔn)規(guī)定情況下，各牌號碳、錳、硅含量可以不作為交貨條件，但其含量應(yīng)在質(zhì)量證明書中注明。 6.1.6 成品鋼材的化學(xué)成分允許偏差應(yīng)符合GB/T 222的規(guī)定。 6.2冶煉方法 鋼由氧氣轉(zhuǎn)爐或電爐冶煉，除非需方有特殊要求，并在合同中注明，冶煉方法一般由供方?jīng)Q定。 6.3交貨狀態(tài) 6.3.1 鋼板及鋼帶以退火后平整狀態(tài)交貨。經(jīng)供需雙方協(xié)議，亦可以硬質(zhì)或半硬質(zhì)以及其他狀態(tài)交貨，此時(shí)力學(xué)性能由供需雙方協(xié)商確定。 6.3.2鋼板及鋼帶通常涂油后供貨，所涂油膜應(yīng)能用堿性或其他常用的除油液去除。在通常的包裝、運(yùn)輸、裝卸及貯存條件下，供方應(yīng)保證對涂油產(chǎn)品自出廠之日起6個(gè)月內(nèi)不生銹。如需方要求不涂油供貨，應(yīng)在訂貨時(shí)協(xié)商。 注：對于需方要求的不涂油產(chǎn)品，在運(yùn)輸、裝卸、儲存和使用過程中表面易產(chǎn)生輕微劃傷及銹蝕。 6.4力學(xué)性能 6.4.1 以退火后平整狀態(tài)交貨的鋼板及鋼帶的橫向拉伸試驗(yàn)應(yīng)符合表3的規(guī)定。如因?qū)挾鹊脑颍谡摪寮颁搸蠠o法截取橫向試樣，則取縱向試樣進(jìn)行拉伸試驗(yàn)，力學(xué)性能合格值由供需雙方協(xié)商確定。 表3力學(xué)性能 牌號 下屈服強(qiáng)度 ReLa/MPa 抗拉強(qiáng)度 Rm/MPa 斷后伸長率b/％ A50 mmc A80 mmd Q195 ≥195 315～430 ≥26 ≥24 Q215 ≥215 335～450 ≥24 ≥22 Q235 ≥235 370～500 ≥22 ≥20 Q275 ≥275 410～540 ≥20 ≥18 Q325 ≥325 510～680 ≥18 ≥16 a當(dāng)屈服現(xiàn)象不明顯時(shí)，可采用規(guī)定塑性延伸強(qiáng)度RP0.2代替。 b需方應(yīng)指明采用A50 mm或A80 mm。未指明時(shí)，采用A80 mm。 c試樣為GB/T 228.1—2010中的P7試樣。 d試樣為GB/T 228.1—2010中的P6試樣。 6.4.2寬鋼板及鋼帶應(yīng)做180°彎曲試驗(yàn)，彎曲壓頭直徑應(yīng)符合表4的規(guī)定。試樣彎曲處的外面和側(cè)面不應(yīng)有目視可見的裂紋。如供方能保證其彎曲性能，可不進(jìn)行該試驗(yàn)。 表4彎曲試驗(yàn) 牌號 彎曲試驗(yàn)a,b 試樣方向 彎曲壓頭直徑D/mm Q195 橫向 0.5a Q215 橫向 0.5a Q235 橫向 1a Q275 橫向 1a Q325 a試樣寬度b≥20 mm，仲裁試驗(yàn)時(shí)b=20 mm。 b a為試樣厚度。 6.5表面質(zhì)量 6.5.1 鋼板及鋼帶表面不得有氣泡、裂紋、結(jié)疤、折疊和夾雜等對使用有害的缺陷。鋼板及鋼帶不應(yīng)有目視可見分層。 6.5.2 鋼板及鋼帶各表面質(zhì)量級別的特征按表5的規(guī)定。 表5表面質(zhì)量級別及特征 級別 名稱 特征 FB 較高級表面 表面允許有少量不影響成形性的缺陷，如小氣泡、小劃痕、小輥印、輕微劃傷及氧化色等允許存在 FC 高級表面 產(chǎn)品兩面中較好的一面應(yīng)對缺陷進(jìn)一步限制，無目視可見的明顯缺陷，另一面應(yīng)達(dá)到FB表面的要求 6.5.3 對于鋼帶，在連續(xù)生產(chǎn)過程中，由于局部的表面缺陷不易發(fā)現(xiàn)和去除，因此允許帶缺陷交貨，但有缺陷部分應(yīng)不超過每卷總長度的6%。 6.6表面結(jié)構(gòu) 6.6.1 鋼帶表面結(jié)構(gòu)分為三種，其特征及要求見表6。 6.6.2 如需方對粗糙度有特殊要求，應(yīng)在訂貨時(shí)協(xié)商。 表6表面結(jié)構(gòu)特征 表面結(jié)構(gòu) 代號 平均粗糙度Ra/μm 超平滑 b ≤0.4 光亮表面 B ≤0.9 麻面 D >0.6～1.9 7試驗(yàn)方法 7.1 鋼的化學(xué)成分試驗(yàn)一般按GB/T 4336、GB/T 20123或通用的化學(xué)分析方法進(jìn)行，仲裁時(shí)采用GB/T 223.3、GB/T 223.9、GB/T 223.11、GB/T 223.18、GB/T 223.19、GB/T 223.23、GB/T 223.37、GB/T 223.58、GB/T 223.59、GB/T 223.60、GB/T 223.63、GB/T 223.64、GB/T 223.68、GB/T 223.71、GB/T 223.72或GB/T 20125的規(guī)定。 7.2每批鋼板及鋼帶的檢驗(yàn)項(xiàng)目、取樣數(shù)量、取樣方法及試驗(yàn)方法應(yīng)符合表7的規(guī)定。 表7 檢驗(yàn)項(xiàng)目、取樣數(shù)量、取樣方法及試驗(yàn)方法 序號 檢驗(yàn)項(xiàng)目 取樣數(shù)量 取樣方法 試驗(yàn)方法 1 化學(xué)成分 1個(gè)/爐 GB/T 20066 見7.1 2 拉伸試驗(yàn) 1個(gè)/批 GB/T 2975 GB/T 228.1—2010 3 彎曲試驗(yàn) 1個(gè)/批 GB/T 2975 GB/T 232 4 表面粗糙度 — GB/T 2975 GB/T 2523 5 尺寸、外形 — — 符合精度要求的適宜量具 6 表面質(zhì)量 逐張/逐卷 — 目視 8檢驗(yàn)規(guī)則 8.1 鋼板及鋼帶的檢查和驗(yàn)收由供方質(zhì)量監(jiān)督檢驗(yàn)部門進(jìn)行。 8.2鋼板及鋼帶應(yīng)成批驗(yàn)收。每批由同一牌號、同一爐號、同一厚度和同一熱處理制度的鋼板及鋼帶組成。寬鋼板及鋼帶每批重量應(yīng)不大于60 t。窄鋼板及鋼帶每批重量應(yīng)不大于30 t。 8.3鋼板及鋼帶的復(fù)驗(yàn)和判定應(yīng)按GB/T 17505的規(guī)定進(jìn)行。 8.4化學(xué)成分和力學(xué)性能檢測結(jié)果按GB/T 8770中的修約值比較法進(jìn)行修約。修約規(guī)則應(yīng)符合GB/T 8170的規(guī)定。 9包裝、標(biāo)志及質(zhì)量證明書 鋼板及鋼帶的包裝、標(biāo)志及質(zhì)量證明書應(yīng)符合GB/T 247的規(guī)定。