標準編號:	JG/T 475-2015
中文名稱:	建筑幕墻用硅酮結構密封膠
英文名稱:	Structural Silicon Sealants for Building Curtain Wall
行業分類:	JG    建筑工業行業標準
發布機構:	中華人民共和國住房和城鄉建設部
發布日期:	2015-11-23
實施日期:	2016-4-1
標準狀態:	valid
翻譯語言:	英文
文件格式:	PDF
中文字符數:	25000 字
翻譯價格(元):	1500.0
交付時間:	付款后 1 個工作日

Structural silicon sealants for building curtain wall 1 Scope This standard specifies the classification and labeling, requirements, test methods, inspection rules, marking, packaging, transportation and storage of structural silicon sealants for building curtain wall (hereinafter referred to as structural silicon sealants). This standard is applicable to structural silicon sealants for building curtain wall with a design service life of not less than 25 years. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. GB/T 528 Rubber, vulcanized or thermoplastic - Determination of tensile stress-strain properties GB/T 531.1 Rubber vulcanized or thermoplastic - Determination of indentation hardness - Part 1: Durometer method (Shore hardness) GB/T 9789 Metallic and other non-organic coatings - Sulfur dioxide test with general condensation of moisture GB 9985 Detergents for hand dishwashing GB/T 10125 Corrosion tests in artificial atmospheres - Salt spray tests GB/T 13477.1 Test method for building sealants - Part 1: Specifications for test substrates GB/T 13477.3 Test method for building sealants - Part 3: Determination of extrudability of sealants using standardized apparatus GB/T 13477.5-2002 Test method for building sealants - Part 5: Determination for track-free time GB/T 13477.6 Test methods for building sealants - Part 6: Determination of flow GB/T 13477.8-2002 Test method for building sealants - Part 8: Determination of tensile properties GB/T 13477.17 Test method for building sealants - Part 17: Determination of elastic recovery GB/T 13477.19 Test method for building sealants - Part 19: Determination of change in mass and volume GB/T 16422.2 Plastics - Methods of exposure to laboratory light sources - Part 2: Xenon-arc sources GB/T 16422.3 Plastics - Methods of exposure to laboratory light sources - Part 3: Fluorescent UV lamps GB 16776-2005 Structural silicon sealants for building JG/T 471 Elastic sealants for insulating glass units of windows and curtain walls in building 3 Classification and labeling 3.1 Classification Products are classified into one-component type (1) and two-component type (2) by composition. Products are classified into aluminum (AL), glass (G) and miscellaneous metals (M) by applicable substrates. 3.2 Labeling Products are labeled in the following order: name, classification, and number of this standard. Example: the two-component structural silicon sealant for building curtain wall of aluminum and glass substrate is labeled as: Structural silicon sealant 2ALG JG/T 475-2015 4 Requirements 4.1 General requirements The design service life of structural silicon sealant shall not be less than 25 years, and the use conditions and maintained properties shall be clearly defined. See Table 1 for the general requirements of products. ? Table 1 General requirements S.N. Item Requirements 1 Stiffness Initial stiffness K12.5 To be reported Stiffness ratio after water-ultraviolet irradiation Kc, 12.5/K12.5 0.5≤Kc, 12.5/K12.5≤1.10 2 Consistency evaluation Thermogravimetric analysis To be reported Infrared spectroscopy To be reported 3 Tensile modulus The tensile adhesion strength at 23℃ with elongation of 5%, 10%, 15%, 20% and 25% shall be reported 4 Elastic modulus at 12.5% To be reported The stiffness and elastic modulus test of structural silicon sealants shall meet the requirements of Annex A. The structural silicon sealants may be tested according to the requirements of Annex D, GB 16776-2005 during construction. 4.2 Appearance 4.2.1 The structural silicon sealants shall be fine and uniform paste or viscous body free of bubbles, caking, crusting or gelatinization, and shall be free of non-dispersible precipitates after stirring. 4.2.2 The colors of various components of the two-component structural silicon sealants shall be obviously different. The product color may also be agreed by the supplier and the purchaser, and shall not be obviously different from that of the sample agreed by them. 4.3 Physical and mechanical properties The physical and mechanical properties of products shall meet those specified in Table 2. Table 2 Physical and mechanical properties ... ... 4.4 Compatibility 4.4.1 The compatibility between structural silicon sealants and accessories for structural assembly system shall meet the requirements of Annex A, GB 16776-2005. 4.4.2 The adhesion between structural silicon sealants and substrates used in practical works shall meet the requirements of Annex B, GB 16776-2005. 4.4.3 The compatibility between structural silicon sealants and the materials they are exposed to shall meet the requirements of Annex B. 5 Test methods 5.1 Basic requirements 5.1.1 Standard test conditions Standard test conditions of the laboratory: temperature of (23±2)℃ and relative humidity of (50±5)%. 5.1.2 Preparation of adhesion specimens 5.1.2.1 Specimen preparation Before specimen preparation, the structural silicon sealants used for test shall be placed for more than 24h under standard conditions. The test substrate shall be cleaned with cleaning agent. Two-component specimens shall be mixed according to the ratio required by the manufacturer.

Foreword i 1 Scope 2 Normative references 3 Classification and labeling 3.1 Classification 3.2 Labeling 4 Requirements 4.1 General requirements 4.2 Appearance 4.3 Physical and mechanical properties 4.4 Compatibility 5 Test methods 5.1 Basic requirements 5.2 Appearance 5.3 Slump 5.4 Track-free time 5.5 Extrudability 5.6 Application life 5.7 Shore hardness A 5.8 Bubble 5.9 Tensile properties 5.10 Shear properties 5.11 Tear strength 5.12 Fatigue cycle 5.13 Mass change - thermal weight loss 5.14 Retention rate of UV-resistant tensile strength 5.15 Alkane plasticizers 5.16 Elastic recovery 5.17 Creep resistance 5.18 Compatibility 6 Inspection rules 6.1 Inspection classification 6.2 Batching 6.3 Sampling 6.4 Judgment rules 7 Marking, packaging, transportation and storage 7.1 Marking 7.2 Packaging 7.3 Transportation 7.4 Storage Annex A (Normative) Elastic modulus test of structural silicone sealants Annex B (Normative) Compatibility with adjacent contact materials Annex C (Normative) Creep resistance

建筑幕墻用硅酮結構密封膠 1 范圍 本標準規定了建筑幕墻用硅酮結構密封膠(簡稱硅酮結構膠)的分類和標記、要求、試驗方法，檢驗規則標志、包裝、運輸和貯存。 本標準適用于設計使用年限不低于25年的建筑幕墻工程用硅酮結構密封膠。 2 規范性引用文件 下列文件對于本文件的應用是必不可少的。凡是注日期的引用文件，僅注日期的版本適用于本文件。凡是不注日期的引用文件，其最新版本(包括所有的修改單)適用于本文件。 GB／T 528 硫化橡膠或熱塑性橡膠 拉伸應力應變性能的測定 GB／T 531.1 硫化橡膠或熱塑性橡膠 壓入硬度試驗方法 第1部分：邵氏硬度計法(邵爾硬度) GB／T 9789 金屬和其他無機覆蓋層 通常凝露條件下的二氧化硫腐蝕試驗 GB 9985 手洗餐具用洗滌劑 GB／T 10125 人造氣氛腐蝕試驗 鹽霧試驗 GB／T 13477.1 建筑密封材料試驗方法 第1部分：試驗基材的規定 GB／T 13477.3 建筑密封材料試驗方法 第3部分：使用標準器具測定密封材料擠出性的方法 GB／T 13477.5-2002 建筑密封材料試驗方法 第5部分：表干時間的測定 GB／T 13477.6 建筑密封材料試驗方法 第6部分：流動性的測定 GB／T 13477.8-2002 建筑密封材料試驗方法 第8部分：拉伸粘結性的測定 GB／T 13477.17 建筑密封材料試驗方法 第17部分：彈性恢復率的測定 GB／T 13477.19 建筑密封材料試驗方法 第19部分：質量與體積變化的測定 GB／T 16422.2 塑料 實驗室光源暴露試驗方法 第2部分：氙弧燈 GB／T 16422.3 塑料 實驗室光源暴露試驗方法 第3部分：熒光紫外燈 GB 16776-2005 建筑用硅酮結構密封膠 JG／T 471 建筑門窗幕墻用中空玻璃彈性密封膠 3 分類和標記 3.1 分類 產品按組成分為單組分型(1)和雙組分型(2)。 產品按適用的基材分為鋁材(AL)、玻璃(G)、其他金屬(M)。 3.2 標記 產品按下列順序標記：名稱、分類，本標準編號。 示例：鋁材和玻璃基材用雙組分建筑幕墻用硅酮結構密封膠標記為： 硅酮結構膠2ALG JG／T 475-2015 4 要求 4.1 一般要求 硅酮結構膠的設計使用年限不應低于25年，應明確規定使用條件及保持的性能特性。產品一般要求見表1。 表1 一般要求 序號 項目 要求 1 剛度 初始剛度K12.5 報告 水-紫外線光照后剛度比Kc，12.5／K12.5 0.5≤Kc，12.5／K12.5≤1.10 2 一致性評價 熱重分析 報告 紅外光譜 報告 3 拉伸模量 報告23℃拉伸粘結性在伸長率為5%，10%，15%，20%和25%時的強度 4 12.5%時彈性模量 報告 硅酮結構膠的剛度和彈性模量試驗應符合附錄A的規定。 施工過程中的硅酮結構膠檢測可按GB 16776-2005附錄D的規定進行。 4.2 外觀 4.2.1 硅酮結構膠應為細膩、均勻膏狀物或粘稠體，不應有氣泡、結塊、結皮或凝膠，攪拌后應無不易分散的析出物。 4.2.2 雙組分硅酮結構膠的各組分的顏色應有明顯差異。產品的顏色也可由供需雙方商定，產品的顏色與供需雙方商定的樣品相比，不應有明顯差異。 4.3 物理力學性能 產品物理力學性能應符合表2的要求。 表2 物理力學性能 序號 項目 技術指標 1 下垂度／mm 垂直 ≤3 水平 無變形 2 表干時間／h ≤3 3 擠出性a／s ≤10 4 適用期b／min ≥20 5 邵氏硬度A 20～60 6 氣泡 無可見氣泡 7 拉伸粘結性 23℃拉伸粘結強度標準值Ru，5／MPa ≥50 拉伸粘結強度保持率／% 80℃ ≥75 －20℃ ≥75 水-紫外線光照 ≥75 NaCl鹽霧 ≥75 SO2酸霧 ≥75 清洗劑 ≥75 100℃7 d高溫 ≥75 粘結破壞面積(所有拉伸粘結性項目)／% ≤10 8 剪切強度 23℃剪切強度標準值Ru，5／MPa ≥0.50 剪切強度保持率／% 80℃ ≥75 －20℃ ≥75 粘結破壞面積(所有剪切性能項目)／% ≤10 9 撕裂性能 拉伸粘結強度保持率／% ≥75 10 疲勞循環 拉伸粘結強度保持率／% ≥75 粘結破壞面積／% ≤10 11 質量變化- 熱失重 熱失重／% ≤6.0 12 烷烴增塑劑 紅外光譜 無烷烴增塑劑 13 彈性恢復率c／％ ≥95 14 耐紫外線拉伸強度保持率c／% ≥75 15 蠕變性能d 91 d受力后位移／mm ≤1 力卸載24 h后最大位移／mm ≤0.1 a 僅適用于單組分產品。 b 僅適用于雙組分產品。 c 僅需要時檢測。 d 僅適用于硅酮結構膠承受所有粘結密封單元的應力，在粘結密封單元底部沒有設置防止粘結失效產生危險用支撐裝置的幕墻系統。 4.4 相容性 4.4.1 硅酮結構膠與結構裝配系統用附件的相容性應符合GB 16776-2005附錄A的規定。 4.4.2 硅酮結構膠與實際工程用基材的粘結性應符合GB 16776-2005附錄B的規定。 4.4.3 硅酮結構膠與相鄰接觸材料的相容性應符合附錄B的規定。 5 試驗方法 5.1 基本規定 5.1.1 標準試驗條件 實驗室的標準試驗條件：溫度(23±2)℃，相對濕度(50±5)%。 5.1.2 粘結性試件制備 5.1.2.1 試件制備準備 制備試件前，用于試驗的硅酮結構膠應在標準條件下放置24 h以上。試驗基材應用清潔劑清潔。雙組分試樣應按生產商要求的比例混合。 5.1.2.2 試件形狀、尺寸和基材 試件應符合圖1的規定，應按產品適用的基材類別選用基材，基材應具有足夠的強度防止彎曲變形破損。基材尺寸可以不同于圖1，但應保持硅酮結構膠粘結體的尺寸為(12±1)mm×(12±1)mm×(50±1)mm： AL類——符合GB／T 13477.1要求，陽極氧化鋁板厚度不小于3 mm； G類——符合GB／T 13477.1要求，清潔、無鍍膜的浮法玻璃，厚度不小于5 mm； M類——供方要求的其他金屬基材。 單位為毫米 說明： 1、2——基材； 3——硅酮結構膠。 圖1 粘結性試件示意圖 5.1.2.3 試件制備 試件應按下列方式制備： a) 應按GB／T 13477.8-2002第7章制備試件，并應按生產商要求使用底涂料。 b) 雙組分硅酮結構膠應均勻無分層，且應充分混合，真空攪拌(真空度：≥0.095 MPa)，混合時間約為5 min。無特殊要求時，混合后應在10 min內完成注模和修整。 c) 每個試件應有一面選用G類基材，在生產商沒有規定時，另一面采用AL類基材。 d) 試驗基材應進行有效清潔。可按生產商指定的清潔劑及清潔方式清潔，也可采用以下方式清潔： ——將試驗基材放入無水丙酮(分析純)中浸泡至少2 h； ——用脫脂紗布蘸取新鮮、潔凈的無水丙酮(分析純)將基材表面擦拭2遍； ——用脫脂紗布蘸取新鮮、潔凈的無水乙醇(分析純)將基材表面擦拭2遍； ——在無水乙醇揮發干涸前用干凈的脫脂紗布擦拭1遍。 5.1.2.4 試件養護 試件應按下列方式養護： a) 制備后的試件在標準試驗條件下放置28 d； b) 在不損壞結構膠試件條件下，養護期間應盡早分離擋塊。 5.1.2.5 試件數量 粘結性試件數量見表3。