標準編號:	GB/T 2072-2007
中文名稱:	鎳及鎳合金帶材
英文名稱:	Nickel and nickel alloy strips
中標分類:	62
行業分類:	GB    國家標準
ICS分類:	77.150.40 77.150.40    鎳和鉻產品 77.150.40
發布機構:	國家標準化委員會 國家質量監督檢驗檢疫總局
發布日期:	2007-7-11
實施日期:	2007-11-1
標準狀態:	superseded
被新標準替代:	GB/T 2072-2020 鎳及鎳合金帶、箔材
被替代日期:	2021-8-1
作廢日期:	2021-08-01
替代舊標準:	GB/T 2072-1993 鎳及鎳合金帶 GB/T 11088-1989 電真空器件用鎳及鎳合金板和帶
翻譯語言:	英文
文件格式:	PDF
中文字符數:	5000 字
翻譯價格(元):	420.0
交付時間:	付款后 1 個工作日

Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative. This standard is formulated by reference to "Nickel and Nickel Alloy Plate, Sheet and Strip" (ISO 6208: 1992), "Nickel Plate, Sheet and Strip" (ASTM B162-99 (2005)) and "Nickel-Copper Alloy (UNS N04400) Plate, Sheet and Strip" (ASTM B127-05). This standard replaces "Nickel and Nickel Alloy Strips" (GB/T 2072 1993) and partially replaces "Nickel and Its Alloy Sheets and Strips for Electronic Tube" (GB/T 11088-1989). Compared with GB/T 2072-1993 and GB/T 11088-1989, major variations in this standard are as follows: - Pure nickel designations N5, N7 and their chemical composition requirements were added. Thereinto, the chemical composition of N5 pure nickel is identical to that of designation NW2201 in ISO standards and designation UNS N02201 in ASTM standards while the chemical composition of N7 pure nickel is identical to that of designation NW2200 in ISO standards and designation UNS N02200 in ASTM standards; - Nickel alloy designation NCu30 and its chemical composition requirements were added. Thereinto, the chemical composition is identical to that of designation NW4400 in ISO standards and designation UNS N04400 in ASTM standards; - The width of strip is uniformly specified as 20mm~250 mm, and thereof the shortest length requirements are specified according to the strip thickness; - Permissible thickness deviation of strip is uniformly specified as two-way deviation; - Mechanical property requirements of strip of partial specifications at ambient temperature were added; - Cupping test requirements of strips of partial specifications were improved. - By reference to ISO standards and ASTM standards, the mechanical property and process property requirements of nickel and nickel alloy whose designations are N5, N7 and NCu30 were newly-added. This standard was proposed by China Non-ferrous Metals Industry Federation. This standard is under the jurisdiction of National Technical Committee on Nonferrous Metals of Standardization Administration of China. This standard was drafted by Baoti Group Co., Ltd. and Shenyang Tongxing Industry Co., Ltd. Chief drafting staffs of this standard: Zhang Pinghui, Huang Yongguang, Li Xianjun, Zhang Mingxiang, Wang Li, Liu Gang and Liu Guanqiang. The National Technical Committee on Nonferrous Metals of Standardization Administration of China is in charge of the explanation of this standard. The previous editions of the standard replaced by this standard are as follows: - GB/T 2072-1980, GB/T 2072-1993. - GB/T 11088-1989. Contents Foreword I 1 Scope 1 2 Normative References 1 3 Requirements 1 4 Test Methods 3 5 Inspection Rules 4 6 Marking, Package, Transportation and Storage 5 7 Order (or Contract) Content 5 Nickel and Nickel Alloy Strips 鎳及鎳合金帶材 1 Scope This standard specifies the requirements, test methods, inspection rules and package, marking, transportation and storage as well as order content of nickel and nickel alloy strips. This standard is applicable to nickel and nickel alloy strips used in instrumentation, telecommunication and electronics industry. 2 Normative References The following standards contain provisions which, through reference in this text, constitute provisions of this national standard. For dated reference, subsequent amendments (excluding amending error in the text) to, or revisions of, any of these publications do not be applied. However, the parties whose enter into agreement according to these specifications are encouraged to research whether the latest editions of these references are applied or not. GB/T 228-2002 Metallic Materials - Tensile Testing at Ambient Temperature GB/T 4156 Metals; Cupping Testing Method (thickness 0.2~2mm) GB/T 5235 Wrought Nickel and Nickel Alloy - Chemical Composition and Forms of Wrought Products GB/T 8647 (All parts) Methods for Chemical Analysis of Nickel GB/T 8888 Wrought Heavy Non-ferrous Metal Products-Packing, Marking, Transporting and Storing YS/T 325 Methods for Chemical Analysis of Nickel-Copper Alloy (NiCu 28-2.5-1.5) 3 Requirements 3.1 Product classification3.1.1 Designation, state and specification The designation, state and specification of products shall be in accordance with those specified in Table 1. Table 1 Designation, State and Specification of Strip Designation State Specification/mm Thickness Width Length a N4,N5,N6,N7,NMg0.1,DN,NSi0.19, NCu40-2-1,NCu28-2.5-1.5,NW4-0.15, NW4-0.1,NW4-0.07,NCu30 Soft Semi-hard (Y2) Hard 0.05~0.15 20~250 ≥5000 >0.15~0.55 ≥3000 >0.55~1.2 ≥2000 a As for strips with thickness of 0.55mm~1.20mm, it is permissible to deliver strips whose weight don’t exceed 15% of the batch weight and length is not less than 1m. 3.1.2 Marking examples The product marks shall be expressed according to the sequence of product name, designation, supply state, specification and standard number. The making examples are listed as follows: Example 1: With thickness of 2.0 mm and width of 150 mm, ordinary soft strip made of NMg0.1 shall be marked as: Nickel strip NMg0.1 M 2.0*150 GB/T 2072 - 2007 Example 2: With thickness of 0.8 mm and width of 200 mm, ordinary semi-hard strip made of NCu28-2.5-1.5 shall be marked as: Nickel strip NCu28-2.5-1.5 Y3 0.8*200 GB/T 2072 - 2007 Example 3 With thickness of 0.2 mm and width of 100 mm, high-level hard strip made of NW 4-0.15 shall be marked as: Nickel strip NW4-0.15 Y high-level 0.2*100 GB/T 2072 - 2007 3.2 Chemical compositions The chemical compositions of products shall meet the requirements of GB/T 5235. 3.3 Physical dimension and permissible deviation 3.3.1 The physical dimension and permissible deviation of strip shall meet the requirements specified in Table 2. 3.3.2 The strip shall be straight and even and slight waves are allowable. The side camber degree of strip shall be no more than 3 mm per meter. 3.3.3 Both sides of a strip shall be flush cut without crack and curling. Table 2 Permissible Dimensional Deviation of Strips In mm Thickness Permissible thickness deviation Permissible width deviation within specified width range Ordinary Higher-level 20~150 >150~250 0.05~0.09 ±0.005 ±0.003 0 -0.6 0 -1.0 >0.09~0.15 ±0.010 ±0.007 >0.15~0.30 ±0.015 ±0.010 >0.30~0.45 ±0.020 ±0.015 >0.45~0.55 ±0.025 ±0.020 >0.55~0.85 ±0.030 ±0.025 >0.85~0.95 ±0.035 ±0.030 >0.95~1.20 ±0.040 ±0.035 0 -1.0 0 -1.5 Note 1: If the demander requires the thickness deviation only be"+" or "-", the value is two times of that in the Table. Note 2: If not specified in contract, the permissible thickness deviation shall be in accordance with the requirements of ordinary grade. 3.4 Mechanical property The mechanical property of strip at ambient temperature shall be in accordance with those specified in Table 3. Table 3 Mechanical Property of Strip at Ambient Temperature Designation Thickness of product/mm /mm State Tensile strength: Rm/(N/mm2) Specified non-proportional elongation strength Rp0.2/(N/mm2) Percentage elongation after fracture /% A11.3 A50 N4, NW4-0.15 NW4-0.1, NW4-0.07 0.25~1.2 Soft (M) ≥345 — ≥30 — Hard (Y) ≥490 — ≥2 — N5 0.25~1.2 Soft (M) ≥350 ≥85a — ≥35 N7 0.25~1.2 Soft (M) ≥380 ≥105a — ≥35 Hard (Y) ≥620 ≥480a — ≥2 N6, DN, NMg0.1 NSi0.19 0.25~1.2 Soft (M) ≥392 — ≥30 — Hard (Y) ≥539 — ≥2 — NCu28-2.5-1.5 0.5~1.2 Soft (M) ≥441 — ≥25 — Semi-hard (Y2) ≥568 — ≥6.5 — NCu30 0.25~1.2 Soft (M) ≥480 ≥195a ≥25 — Semi-hard (Y2) ≥500 ≥300a ≥25 — Hard (Y) ≥680 ≥620a ≥2 — NCu40-2-1 0.25~1.2 Soft (M) Semi-hard (Y2) Hard (Y) As measured — As measured — Note: Where the demander has other requirements on the performance, parameters shall be determined through negotiation of both sides. a The specified non-proportional elongation strength is not suitable to the strip whose thickness is less than 0.5 mm. 3.5 Processing properties Except NCu28-2.5-1.5, NCu40-2-1 and NCu30, if the demander requires and notes it in contract, cupping test on the soft strips of other designations, shall be carried out. The punch diameter is 10mm and the results shall be in accordance with those specified in Table 4. Table 4 Cupping test of Strip Thickness of strip 0.10~0.20 >0.20~0.55 >0.55~1.20 Cupping depth, not less than 7.5 8.0 8.5 3.6 Surface quality 3.6.1 The surface of strips shall be smooth and clean, and shall be free from layering, crack, peeling, bubble, thorn, fold or inclusion. 3.6.2 The following defects are allowed on the surface of strips, including slight partial scratch, stain, pit, indentation, roll mark and grinding mark which will not make the permissible deviation of strip thickness exceeded. 3.6.3 Slight oxidation tint, shade and partial slight oil stain on the surface of strips are not regarded a basis for the relevant discard.

Foreword I 1 Scope 2 Normative References 3 Requirements 4 Test Methods 5 Inspection Rules 6 Marking, Package, Transportation and Storage 7 Order (or Contract) Content

ICS 77. 150. 40 H 62 中華人民共和國國家標準 GB/T 2072—2007 代替GB/T 2072—1993 部分代替GB/T 11088—1989 _______________________________________________________________________________ 鎳及鎳合金帶材 Nickel and nickel alloy strips 2007-04-30發布 2007-11-01實施 中華人民共和國國家質量監督檢驗檢疫總局 發布 中 國 國 家 標 準 化 管 理 委 員 會 前 言 本標準參考ISO 6208：1992《鎳及鎳合金厚板、薄板和帶材》、ASTM B162—99 (2005)《鎳厚板、薄板和帶材》及ASTM B127—05《鎳銅合金(UNS N04400)厚板、薄板和帶材》。 本標準代替GB/T 2072 1993《鎳及合金帶》，并部分代替GB/T 11088—1989《電真空器件用鎳及鎳合金板和帶》。 本標準與GB/T 2072—1993和GB/T 11088—1989相比，主要有如下變動： ——增加了純鎳牌號N5、N7及其化學成分要求。其中N5牌號的化學成分等同ISO標準的NW2201牌和ASTM標準的UNS N02201牌號的要求，N7牌號的化學成分等同ISO標準的NW2200牌號和ASTM標準的UNS N02200牌號的要求； ——增加了鎳合金牌號NCu30及其化學成分要求，其化學成分等同ISO標準的NW4400牌號和ASTM標準的UNS N04400牌號的要求； ——帶材的寬度統一規定為20 mm～250 mm，根據帶材厚度規定了其最短長度要求； ——帶材的厚度允許偏差統一規定為雙向偏差； ——增加了部分規格帶材的室溫力學性能要求； ——提高了部分規格帶材的杯突試驗要求。 ——參考ISO標準和ASTM標準，新增了鎳及鎳合金牌號N5、N7和NCu30的力學性能、工藝性能要求。 本標準由中國有色金屬工業協會提出。 本標準由全國有色金屬標準化技術委員會歸口。 本標準由寶鈦集團有限公司、沈陽銅興產業有限公司負責起草。 本標準主要起草人：張平輝、黃永光、李獻軍、張明祥、王麗、劉剛、劉關強。 本標準由全國有色金屬標準化技術委員會負責解釋。 本標準所代替標準的歷次版本發布情況為： ——GB/T 2072—1980、GB/T 2072—1993。 ——GB/T 11088—1989。 鎳及鎳合金帶材 1 范圍 本標準規定了鎳及鎳合金帶材的要求、試驗方法、檢驗規則和包裝、標志、運輸、貯存及訂貨單內容等。 本標準適用于儀表、電訊及電子工業部門用的鎳及鎳合金帶材。 2 規范性引用文件 下列文件中的條款通過本標準的引用而成為本標準的條款。凡是注日期的引用文件，其隨后所有的修改單（不包括勘誤的內容）或修訂版均不適用于本標準，然而，鼓勵根據本標準達成協議的各方研究是否可使用這些文件的最新版本。凡是不注日期的引用文件，其最新版本適用于本標準。 GB/T 228—2002 金屬材料 室溫拉伸試驗方法 GB/T 4156 金屬杯突試驗方法(厚度0.2～2 mm) GB/T 5235 加工鎳及鎳合金 化學成分和產品形狀 GB/T 8647(所有部分) 鎳化學分析方法 GB/T 8888 重有色金屬加工產品的包裝、標志、運輸和貯存 YS/T 325 鎳銅合金(NiCu28-2.5-1.5)化學分析方法 3 要求 3.1 產品分類 3.1.1 牌號、狀態、規格 產品的牌號、狀態和規格應符合表1的規定。 表1 帶材的牌號、狀態、規格 牌 號 狀 態 規格／mm 厚度 寬度 長度a N4,N5,N6,N7,NMg0.1,DN,NSi0.19, NCu40-2-1,NCu28-2.5-1.5,NW4-0.15, NW4-0.1,NW4-0.07,NCu30 軟態(M) 半硬態(Y2) 硬態(Y) 0.05～0.15 20～250 ≥5000 >0.15～0.55 ≥3000 >0.55～1.2 ≥2000 a 厚度為0.55 mm～1.20 mm的帶材，允許交付不超過批重15%的長度不短于1m的帶材。 3.1.2 標記示例 產品標記按產品名稱、牌號、供應狀態、規格和標準編號的順序表示。標記示例如下： 示例1： 用NMg0.1制造的、軟態的、厚度為2.0 mm、寬度為150 mm的普通級帶材，標記為： 鎳帶NMg0.1 M 2.0×150 GB/T 2072—2007 示例2： 用NCu28-2.5-1.5制造的、半硬態的、厚度為0.8 mm、寬度為200 mm的普通級帶材，標記為： 鎳帶NCu28-2.5-1.5 Y3 0.8×200 GB/T 2072—2007 示例3： 用NW4-0.15制造的、硬態的、厚度為0.2 mm、寬度為100 mm的較高級帶材，標記為： 鎳帶NW4-0.15 Y較高級 0.2×100 GB/T 2072—2007 3.2 化學成分 產品的化學成分應符合GB/T 5235的規定。 3.3 外形尺寸及尺寸允許偏差 3.3.1 帶材的外形尺寸及尺寸允許偏差應符合表2的規定。 3.3.2 帶材應平直，允許有輕微的波浪。帶材的側邊彎曲度每米不大于3 mm。 3.3.3 帶材的兩邊應切齊，無裂邊和卷邊。 表2 帶材的尺寸允許偏差 單位為毫米 厚 度 厚度允許偏差 規定寬度范圍的寬度允許偏差 普通級 較高級 20～150 >150～250 0.05～0.09 ±0.005 ±0.003 0 －0.6 0 －1.0 >0.09～0.15 ±0.010 ±0.007 >0.15～0.30 ±0.015 ±0.010 >0.30～0.45 ±0.020 ±0.015 >0.45～0.55 ±0.025 ±0.020 >0.55～0.85 ±0.030 ±0.025 >0.85～0.95 ±0.035 ±0.030 >0.95～1.20 ±0.040 ±0.035 0 －1.0 0 －1.5 注1：當需方要求厚度偏差僅為“+”或“－”時，其值為表中數值的2倍。 注2：若合同中未注明時，厚度允許偏差按普通級執行。 3.4 力學性能 帶材的縱向室溫力學性能應符合表3的規定。 表3 帶材的室溫力學性能 牌 號 產品厚度/mm 狀態 抗拉強度 Rm/(N/mm2) 規定非比例延伸強度 Rp0.2/(N/mm2) 斷后伸長率/% A11.3 A50 N4,NW4-0.15 NW4-0.1,NW4-0.07 0.25～1.2 軟態(M) ≥345 — ≥30 — 硬態(Y) ≥490 — ≥2 — N5 0.25～1.2 軟態(M) ≥350 ≥85a — ≥35 N7 0.25～1.2 軟態(M) ≥380 ≥105a — ≥35 硬態(Y) ≥620 ≥480a — ≥2 N6,DN,NMg0.1 NSi0.19 0.25～1.2 軟態(M) ≥392 — ≥30 — 硬態(Y) ≥539 — ≥2 — NCu28-2.5-1.5 0.5～1.2 軟態(M) ≥441 — ≥25 — 半硬態(Y2) ≥568 — ≥6.5 — NCu30 0.25～1.2 軟態(M) ≥480 ≥195a ≥25 — 半硬態(Y2) ≥500 ≥300a ≥25 — 硬態(Y) ≥680 ≥620a ≥2 — NCu40-2-1 0.25～1.2 軟態(M) 半硬態(Y2) 硬態(Y) 報實測 — 報實測 — 注：需方對性能有其他要求時，指標由雙方協商確定。 a 規定非比例延伸強度不適于厚度小于0.5 mm的帶材。 3.5 工藝性能 除NCu28-2.5-1.5、NCu40-2-1、NCu30外，當需方要求并在合同中注明時，其他牌號的軟態帶材可進行杯突試驗，沖頭直徑為10mm，其結果應符合表4的規定。 表4 帶材的杯突試驗 帶材厚度 0.10～0.20 >0.20～0.55 >0.55～1.20 杯突深度，不小于 7.5 8.0 8.5 3.6 表面質量 3.6.1 帶材表面應光滑、清潔，不危許有分層、裂紋、起皮、氣泡，起刺、壓折和夾雜。 3.6.2 帶材表面允許有輕微的且不使帶材厚度超出允許偏差的局部的劃傷、斑點、凹坑、壓入物和輥印、修磨痕跡等缺陷。 3.6.3 帶材表面的輕微氧化色、發暗和局部的輕微油跡，不作為報廢的依據。 4 試驗方法 4.1 帶材的化學成分仲裁分析方法按GB/T 8647、YS/T 325或供需雙方商定的其他方法進行。 4.2 帶材的力學性能試驗按GB/T 228進行。比例試樣選P04試樣，非比例試樣選P5試樣。 4.3 帶材的杯突試驗按GB/T 4156進行， 4.4 帶材的外形尺寸用相應精度的量具進行測量，厚度在距端部不小于100 mm和距邊部不小于5 mm處測量（寬度小于50 mm的帶材在距邊部不小于3 mm處測量），測量范圍以外的厚度超差不作為報廢的依據。 4.5 帶材的表面質量用目視檢查。 5 檢驗規則 5.1 檢查和驗收 5.1.1 帶材應由供方技術監督部門進行檢驗，保證產品質量符合本標準的規定，并填寫質量證明書。5.1.2 需方應對收到的產品按本標準的規定進行檢驗。檢驗結果與本標準及訂貨合同的規定不符時，應以書面形式向供方提出，由供需雙方協商解決。屬于表面質量及尺寸偏差的異議，應在收到產品之日起一個月內提出，屬于其他性能的異議，應在收到產品之日起三個月內提出。如需仲裁，仲裁取樣應由供需雙方共同進行。 5.2 組批 帶材應成批提交驗收，每批應由同一牌號、狀態和規格的產品組成，其批重應不大于2000 kg。 5.3 檢驗項目 每批帶材應進行化學成分、外形尺寸、力學性能和表面質量的檢驗。當需方要求并在合同中注明時，帶材應進行工藝性能的檢驗。 5.4 取樣 帶材的取樣應符合表5的規定。 表5 取樣規定 檢驗項目 取樣規定 要求的章條號 試驗方法的章條號 化學成分 每批帶材上取1個樣。允許供方以原鑄錠或坯料的分析結果報出 3.2 4.1 室溫拉伸 每批帶材任取2卷，每卷沿軋制方向取1個試樣 3.4 4.2 杯突 每批帶材任取2卷，每卷取1個試樣 3.5 4.3 外形尺寸 逐卷 3.3 4.4 表面質量 逐卷 3.6 4.5 5.5 檢驗結果的判定 5.5.1 化學成分不合格時，判該批產品不合格。 5.5.2 帶材尺寸偏差、表面質量不合格時，判該卷產品不合格。 5.5.3 力學性能和工藝性能試驗結果中若有試樣不合格時，應從該批帶材中取雙倍數量的試樣進行重復試險。重復試驗結果全部合格時，則判該批產品合格；若重復試驗仍有試樣不合格時，則判該批產品不合格，但允許供方逐卷檢驗，合格者組批交貨。 6 標志、包裝、運輸和貯存 6.1 標志 每件產品應附有標簽或標牌，其上注明： b) 生產廠名稱； c) 產品牌號、規格和狀態； d) 產品批號。 6.2 包裝、包裝標志、運輸和貯存 產品的包裝、包裝標志、運輸和貯存應符合GB/T 8888的規定。 6.3 質量證明書 a) 供方名稱、地址； b) 產品名稱； c) 產品牌號、規格和狀態； d) 批號； e) 凈重和件數； f) 各項分析檢驗結果和技術監督部門印記； g) 本標準編號； h) 出廠日期（或包裝日期）。 7 訂貨單（或合同）內容 訂購本標準所列材料的訂貨單（或合同）內應包括下列內容： a) 產品名稱； b) 牌號和狀態； c) 規格尺寸及尺寸允許偏差的精度等級； d) 產品凈重； e) 杯突試驗； f) 本標準編號； g) 其他。 ___________________________________