標準編號:	GB/T 2573-1989
中文名稱:	玻璃纖維增強塑料大氣暴露試驗方法
英文名稱:	Test method for atmosphere exposure of glass fiber reinforced plastics
行業分類:	GB    國家標準
發布日期:	1989-03-17
實施日期:	1989-12-1
標準狀態:	superseded
被新標準替代:	GB/T 2573-2008 玻璃纖維增強塑料老化性能試驗方法
翻譯語言:	英文
文件格式:	PDF
中文字符數:	4000 字
翻譯價格(元):	720.0
交付時間:	付款后 1 個工作日

Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative. This standard is developed by reference to ISO 4607-1978 Plastics - Methods of exposure to natural weathering. Test method for atmosphere exposure of glass fiber reinforced plastics 1 Subject content and applicable scope This standard specifies exposed pieces, exposure site, exposure racks, test procedure, and result calculation for atmosphere exposure test of glass fiber reinforced plastics. This standard is applicable to the evaluation of the influence of atmosphere exposure on the appearance and physical or mechanical performances of glass fiber reinforced plastics at the state without applied stress. 2 Normative references GB 1446 Fiber-reinforced plastics composites - The generals for determination of properties 3 Exposed pieces 3.1 Specimen, specimen plate, or physical objects may be used as the exposed pieces for atmosphere exposure test. 3.2 The specimen shall meet the requirements of GB 1446. 3.3 The dimension of the specimen plate shall be calculated according to the dimension and quantity required by the performance test, and the edge of 20 to 30 mm shall be added. 3.4 The physical object shall meet the requirements of the exposure site and the specimen processing method shall be specified. 3.5 The exposed pieces, before the test, shall be sampled according to the performance requirements, initial performance shall be determined under standard atmospheres, and then the quantity of exposed pieces to be tested shall be determined according to the exposure duration, contrast group number and other relevant requirements. It is recommended to carry out calculation according to twice of the exposed quantity, among which one half of pieces are used for exposure test and the other half for indoor shelf test; after a certain period, all the pieces shall be sampled at the same time and be determined for their performances under the same conditions so as to perform indoor and outdoor performance comparison. 3.6 Unless otherwise specified, the number of exposed pieces in each group shall not be less than 5. 3.7 The exposed pieces, in addition to being sampled from the same batch, shall also be sampled and grouped randomly. 4 Exposure site 4.1 The places with representative climate types or with environment conditions similar to that of the actual use shall be selected as the exposure site. 4.2 Exposure site shall be flat and shall not be affected by high-rise structures. If there are obstacles around, the distance between the exposed site and the obstacle shall be greater than three times the height of the obstacle. 4.3 Exposure site shall maintain the vegetation status of local natural environment, mainly of grass ground, and the grass height should not exceed 30 cm. If there is snow, do not destroy it artificially. 4.4 Exposure site is allowed to be placed on the roof of the building, but the materials used for the roofing platform must be stated in the test report. 4.5 Meteorological observation instruments shall be provided at the same time when the exposure site is arranged, and observation shall be conducted. The installation and observation methods of relevant meteorological observation instruments shall be carried out according to Specifications for Surface Meteorological Observation and Specifications for Solar Radiation Observation promulgated by China Meteorological Administration. If there is a meteorological observatory (station) near the exposure site, the observation data may be used directly. Atmospheric meteorological data shall include: air temperature (mean, maximum, minimum), air pressure, relative humidity, total precipitation, average wind velocity, sunshine duration, sunshine percentage, total horizontal solar radiation, land surface temperature (mean, maximum, minimum), monthly and annual mean values (or cumulative values) of acid rain. Exposure sites with special environment may be subject to additional observation items as required. 4.6 Contrast exposures shall be kept indoors near the exposure site without direct sunlight. 5 Exposed rack and fixing method of exposed pieces 5.1 The exposed rack is used to place exposed pieces. See the following figure for the structure.

Foreword i 1 Subject content and applicable scope 2 Normative references 3 Exposed pieces 4 Exposure site 5 Exposed rack and fixing method of exposed pieces 6 Test procedure 7 Result calculation 8 Test report Additional explanation

中華人民共和國國家標準 玻璃纖維增強塑料 大氣暴露試驗方法 Test method for atmosphere exposure of glass fiber reinforced plastics GB 2573—89 代替GB 2573—81 本標準參照采用ISO 4607—1978《塑料——自然老化曝曬方法》。 1 主題內容與適用范圍 本標準規定了玻璃纖維增強塑料大氣暴露試驗的暴露件、暴露場，暴露架、試驗步驟和結果計算。 本標準適用于評定在無外加應力狀態下大氣暴露對玻璃纖維增強塑料的外觀、物理或力學性能的影響。 2.引用標準 GB 1446纖維增強塑料性能試驗方法總則 3 暴露件 3.1 大氣暴露試驗用的暴露件可直接用試樣，試樣板或實物。 3.2試樣應符合GB 1446的規定。 3.3試樣板尺寸按性能試驗要求的尺寸和數量計算，另加邊緣20～30 mm。 3.4 實物應適合暴露場要求，且應規定試樣加工方法。 3.5 暴露件在暴露試驗前，應按性能要求取樣，在標準環境下測定初始性能，然后按投放年限、對比組數等要求，確定投放量。建議按投放暴露量的兩倍計算，即其中一半作暴露試驗用，另一半作室內存放試驗用，經一定期齡后，兩者同時取樣，并在相同條件下測定性能，以作室內外性能對比。 3.6 除非另有規定，每組暴露件不得少于5個。 3.7 暴露件除應具有同批性外，還應隨機取樣、分組。 4.暴露場 4.1 暴露場應選擇有代表性的氣候類型或與實際使用環境條件相近似的地方。 4.2 暴露場四周要平坦，不為高聳物所影響。如周圍有障礙物時，應距離該障礙物高度的三倍以上。 4.3 暴露場要保持當地自然環境植被狀態，以草地面為主，草高不宜超過30 cm。如有積雪現象，不要人為破壞。 4.4 暴露場允許設在建筑物屋頂平臺上，但必須在試驗報告中說明屋面平臺所用材料。 4.5 設置暴露場時，要同時設置氣象觀測儀器，并進行觀測。有關氣象儀器安裝及觀測方法均按中央氣象局頒布的《地面氣象觀察規范》和《日射觀測規范》進行。暴露場附近有氣象臺(站)的，可直接利用其觀測資料。 大氣氣象資料應包括：氣溫(平均、最高、最低)、氣壓、相對濕度、總降水量，平均風速、日照時數、日照百分率，水平面太陽總輻射、地表面溫度(平均、最高、最低)、酸雨的月和年平均值(或累計值)。 特殊環境的暴露場可按要求增加觀測項目。 4.6 對比暴露件保存在暴露場附近無陽光直射的室內。 5 暴露架及暴露件固定方法 5.4 暴露架用于放置暴露件。結構參見下圖。 1—固定試樣用孔(4 mm)；2—角鋼(30 mm×30 mm×3 mm)二條焊接成⊥型 (其余架材全用角鋼40 mm×40 mm×4 mm焊接)； α—暴露角；A—最低邊離地距離；B—架水平深度； H—最高邊離地距離；L—架寬度 5.2 暴露架可用鋁合金或玻璃纖維增強塑料型材制造，結構力求簡單，牢固耐用，能經受當地最大風力作用，且與地面固定。 5.3 暴露架面最低邊離地、屋面的距離不小于： 草地面暴露場 0.5 m 屋面暴露場 0.8 m 5.4 暴露架面的方位朝正南。架面與水平的傾角(即暴露角)應等于場地的地理緯度，也允許采用45°，準確度±1°。 5.5 暴露架行距在北緯35°以南地區為1.5 m以上，以北地區為2.5 m以上，以互不遮陽為原則。 5.6 暴露件用絕緣白瓷瓶或其他合適部件固定在暴露架面上，松緊應適度，不應對其產生有害影響。用其他方式固定時，上下兩端部要無應力地固定在暴露架面上，兩端被遮蔽的長度不應超過試樣總長度的十分之一，更不能遮蔽其工作部位。 5.7 暴露件不改換暴露面，不帶背板。 5.8 暴露件上下兩行之間至少相距10mm。 5.9 暴露件編號用不易剝落的涂料書寫在其背面左上角或在暴露架相應位置掛牌。 5.10 實物可按實際使用要求暴露。 6 試驗步驟 6.1 暴露試驗前檢查暴露件初始外觀(如顏色、光澤、纖維顯露情況、裂痕、孔洞、氣泡等)。按要求測試初始性能。 6.2 暴露件投放時間最好選擇在當地每年溫度、相對濕度同時出現較高值的季節，也可根據具體要求選擇其他季節。 6.3 暴露件固定方法按第5章規定。 6.4 暴露件的檢測期齡一般不少于5年。可按下列期齡(年)取樣；0.5，1，2，3，5，7，10……。 6.5 暴露試驗期間前兩年每月對暴露件進行一次外觀檢查，以后檢查間隔可適當延長，但至少每半年檢查一次。檢查前可用毛刷或軟紗團輕擦表面，如積塵太多，可用水濕紗團輕抹表面，但不得將其放入水中清洗。 6.6 暴露到規定期齡后，對暴露件進行外觀檢查。從試樣板或實物上加工試樣應符合GB 1446第1章規定。若加工時用水冷卻，應及時擦干。 6.7 按試驗要求測試性能前，待測試樣應按GB 1446第3章規定進行狀態調節，否則，應在試驗報告中說明。 6.8 不允許在雨天取樣，如遇雨天，取樣時間向后適當推移。暴露件從取樣到測試完畢，不得超過5天，在此期間，可保存在暴露場附近的室內。 6.9 當測試與外觀有關的性能時，應說明測試面的狀態；測試彎曲或沖擊性能時，應將試樣的暴露面作為受壓面或受沖擊面。 7 結果計算 7.1 按GB 1446第6章的規定計算每組試樣的算術平均值和標準差。 7.2 性能保留率按下式計算，保留二位有效數字： 式中：Ri——暴露i期齡后性能保留率，％； ——試樣的初始性能算術平均值； ——暴露i期齡后每組試樣性能算術平均值。 8試驗報告 試驗報告應包括下列各項中的全部或部分： a.說明試驗按本標準進行； b.試驗項目名稱； c.暴露件來源、制備、品種和規格； d.暴露件編號，試驗前后及試驗期間外觀； e.試驗場、緯度、暴露角及暴露期間的氣象資料； f.暴露件投放時間和期齡； g.每組試樣的數量、單值、算術平均值、標準差和性能保留率，性能測定時的環境狀態(溫度、相對濕度)和試樣狀態調節； h.試驗人員、日期及其他。 附加說明： 本標準由全國纖維增強塑料標準化技術委員會提出并歸口。 本標準由廣東省建筑科研設計所負責起草。 本標準主要起草人祝啟偉。